LUMINESCENCE OF ALUMINUM OXIDE FILMS AND PERSPECTIVES OF THEIR APPLICATION IN NANOPHOTONICS PLANAR MICROSTRUCTURES
Abstract
Various methods of fabrication the luminescent film structures based on porous anodic alumina are analyzed. Manufacturing of luminescent structures by anodizing aluminum in oxalic acid allows observation of visible to the naked eye photoluminescence in the blue range, which remains under ambient conditions for a year or longer. Alumina xerogel prepared in a form of powder demonstrates luminescence in the blue range, which disappears totally after annealing at 800 ºC. Photoluminescence of porous anodic alumina which contains terbium ions in the xerogel of alumina or deposited from solutions of salts formed in the anodic alumina pores has been investigated. The perspectives of formation of planar microstructures using a porous anodic alumina supporting electromagnetic whispering gallery modes are discussed.
About the Authors
L. S. Khoroshko
Белорусский государственный университет информатики и радиоэлектроники
Belarus
Belarus
T. I. Orekhovskaya
Белорусский государственный университет информатики и радиоэлектроники
Belarus
Belarus
M. V. Meledina
Белорусский государственный университет информатики и радиоэлектроники
Belarus
Belarus
I. A. Nikolaenko
Белорусский государственный университет информатики и радиоэлектроники
Belarus
Belarus
A. S. Kochev
Белорусский государственный университет информатики и радиоэлектроники
Belarus
Belarus
A. M. Asharif
Белорусский государственный университет информатики и радиоэлектроники
Belarus
Belarus
B. S. Kolosnitsyn
Белорусский государственный университет информатики и радиоэлектроники
Belarus
Belarus
N. V. Gaponenko
Белорусский государственный университет информатики и радиоэлектроники
Belarus
Belarus
A. V. Mudry
Институт физики твердого тела и полупроводников НАН Беларуси
Belarus
Belarus
References
1. Cai M., Painter O., Vahala K.J. // Optics letters. 2000. Vol. 25, №19. P. 1430-1432.
2. Vahala K.J // Nature. 2003. Vol. 424. P. 839-846.
3. Gaponenko S. V. // Introduction to Nanophotonics. Cambridge University Press. 2010. P. 484.
4. Polman A., Min B., Kalkman J. et al. // Appl. Phys. Lett. 2004. Vol. 84, №7. P. 1037-1039.
5. Yang L., Armani D.K // Appl. Phys. Lett. 2003. Vol. 83, №5. P. 825.
6. Knight J. C., Dubreuil N., Sandoghdar V. et al. // Optics Letters. 1996. Vol. 21, №10. P. 698-700.
7. Гапоненко Н.В. Пленки, сформированные золь-гель методом на полупроводниках и в мезопористых матрицах. Мн., 2003.
8. Позняк А.А. Модифицированный анодный оксид алюминия и композитные материалы на его основе. Мн., 2007.
9. Сокол В.А. Анодные оксиды алюминия. Мн., 2011.
10. Wu J.H, Wu X.L., Tang N. et al. // Appl. Phys. А. 2001. Vol. 72. P. 735-737.
11. Du Y., Cai W.L., Mo C.M. et al. // Appl. Phys. Lett. 1999. Vol. 74, №20. P. 2951-2953.
12. Кортов В.С., Мильман И.И., Никифоров С.В. и др. // Физика твердого тела. 2004. Т. 46, №12. С. 2143-2147.
13. Кортов В.С. , Мильман И.И. , Никифоров С.В. // Физика твердого тела. 1997. Т. 39, №9. С. 1538-1543.
14. Кортов В.С., Мильман И.И., Никифоров С.В. и др. // Физика твердого тела. 2003. Т. 45, № 7. С. 1202-1208.
15. Gaponenko N.V., Kortov V.S., Smirnova N.P. et al. // Microelectronic Engineering. 2012. Vol. 90. P. 131-137.
Review
For citations:
Khoroshko L.S., Orekhovskaya T.I., Meledina M.V., Nikolaenko I.A., Kochev A.S., Asharif A.M., Kolosnitsyn B.S., Gaponenko N.V., Mudry A.V. LUMINESCENCE OF ALUMINUM OXIDE FILMS AND PERSPECTIVES OF THEIR APPLICATION IN NANOPHOTONICS PLANAR MICROSTRUCTURES. Doklady BGUIR. 2012;(5):16-20. (In Russ.)
Views: 1487
Email this article 